Short curing time bulk fill composite systems: volumetric shrinkage, degree of conversion and Vickers hardness.

This study aimed to evaluate volumetric polymerization shrinkage, degree of conversion and Vickers hardness of four bulk-fill resin composites light-activated with their dedicated light curing units (LCUs). Four groups were evaluated, according to the type of composite and curing mode: Tetric EvoCeram Bulk-fill (TEBO) and Tetric EvoFlow Bulk-fill (TEBF) were light-activated with Bluephase Style 20i (20s, in high-mode), while Tetric Powerfill (TEPO) and Tetric Powerflow (TEPF) were light-activated with Bluephase PowerCure (3s). Volumetric polymerization shrinkage test (n = 6) was performed in standardized box-shaped class-I cavities of extracted third molars (4 x 4 x 4 mm). Teeth were scanned before and after resin composite application by micro-computed tomography, and acquired data were evaluated with Amira software. Degree of conversion (n = 5) was evaluated at the top and bottom surfaces of composite cylindric samples (4 mm diameter, 4 mm thickness) using an FT-IR spectrometer (spectra between 1,500 and 1,800 cm-1, 40 scans at a resolution of 4 cm-1). Three Vickers indentations (50 g / 15 s), spaced 500 µm apart, were performed on the top and bottom composite surfaces and averaged. One-way ANOVA was used for data evaluation. TEPF showed the lowest volumetric polymerization shrinkage (p < 0.05), while the other composites were not significantly different within each other (p > 0.05). All materials presented a significant decrease in degree of conversion and Vickers hardness when compared top to bottom surfaces (p < 0.05). Bottom to top surface ratios for degree of conversion ranged from 0.8 (TEBO and TEPO) to 0.9 (TEBF and TEPF), and from 0.4 (TEPO) to 0.7 (TEBF and TEPF) for hardness. In conclusion, resinous materials present a decrease in hardness and degree of conversion from top to bottom even when a higher power is used, while the flowable material TEPF showed the lowest volumetric shrinkage values compared to the other materials.

The Influence of Adhesive Strategy, Type of Dental Composite, and Polishing Time on Marginal Gap Formation in Class I-like Cavities.

Even after more than six decades of dental composite invention (1962), there is still controversial information about the time in which composite restorations should be polished in order to avoid marginal gap formation at the tooth-composite interface. The aim of the present study was to analyze the influence of adhesive strategy, the type of dental composite, and polishing time on marginal gap formation (%MG) at the tooth-composite interface. Class I-like cavities were hybridized with a universal adhesive system (Single Bond Universal) through two strategies: selective enamel etching (SEE) or self-etching mode (SEM). Cavities were filled with two types of dental composites: nanofilled (Z350) or bulk fill (Filtek One Bulk Fill-ONE), and polishing was performed immediately or delayed for 7 days (n = 5). %MG was evaluated by using a 3D laser confocal microscope. As flexural modulus (FM) and degree of conversion (DC%) are determinants of marginal integrity in dental composite restorations, these properties were evaluated for both composites. Data were analyzed by ANOVA and Tukey's HSD test (α = 0.05). Cavities hybridized following the SEE strategy presented lower %MG (p < 0.05). Z350 showed higher %MG than ONE (p < 0.05). There was no difference in %MG between the polishing times when the SEE strategy was used (p > 0.05). Z350 presented higher FM than ONE (p < 0.05). DC% was found to be not significant (p > 0.05). The results suggest that selective enamel etching (SEE) is a better strategy for producing less %MG in composite restorations with enamel margins irrespective of the time in which the restoration is polished.

Effect of oral exposure on chemical, physical, mechanical, and morphologic properties of clear orthodontic aligners

The dental industry is heavily committed to developing more esthetic solutions for orthodontic treatments. Invisalign is a system of transparent orthodontic aligners introduced as an alternative to conventional orthodontic fittings with brackets and metal wires. This study aimed to assess the chemical, physical, mechanical and morphologic changes in these polymeric aligners after exposure to the oral environment. Twenty-four Invisalign orthodontic aligners were equally divided into 2 groups: an in vivo aged group in which patients used aligners for 14 days and the reference group, unexposed to the oral environment. Different experimental techniques were used to study the chemical structure, the color changes and translucency, the density and subsequent volume of the aligners, mechanical properties, surface roughness, morphology and elemental composition. The data were subjected to several statistical analyses. Clear orthodontic aligners exhibit chemical stability but undergo a statistically significant optical change in color and translucency. There was a gradual increase in the water absorption rate and the dimensional variation of the polymer, indicating a strong correlation among these factors. The mechanical properties of the polymer showed a statistically significant decrease in its elastic modulus and hardness. There was a slight tendency toward increased surface roughness of the material, but no statistical differences were found between reference and aged groups. The surface morphology of the used aligners demonstrates microcracks, distortions and biofilm formation. Intraoral aging adversely affected the physical, mechanical, and morphologic properties of the Invisalign appliance.

Manufacturing and characterization of a 3D printed lithium disilicate ceramic via robocasting: A pilot study.

OBJECTIVE: The objective of this study was to manufacture and to evaluate the physico-mechanical properties of the Lithium disilicate (Li2O5Si2) ceramic structures fabricated using additive manufacturing (3D printing). METHODS: Li2O5Si2 samples were divided into (n = 30/group): SM (subtractively manufactured) and AR (additive/robocasting). For the AR group, Li2O5Si2 powder was combined with ammonium polyacrylate, hydroxypropyl methylcellulose, and polyelectrolyte to create a colloidal gel, which was then used for printing. A digital CAD model of a disc was designed, and the G-code transferred to a custom built DIW 3D printer. The control group samples were prepared using pre-crystallized ceramic blocks, which were cut to obtain discs with same dimensions as the AR group. Disc-shaped specimens from both groups were crystallized at 840 °C. Mechanical properties were evaluated using biaxial flexural strength test (BFS) and Vickers hardness test. Representative fractographic images of the specimens were acquired using scanning electron microscopy (SEM) to analyze the fracture origin and crack propagation. Energy-dispersive X-ray spectroscopy (EDS) and attenuated total reflection Fourier transform infrared spectroscopy (FTIR-ATR) were used for chemical analysis, and X-ray diffractometry (XRD) was performed to analyze the crystalline phases. RESULTS: AR group yielded lower values of BFS (120.02 MPa ±33.91) and hardness (4.07 GPa ±0.30), relative to the SM group, (325.09 MPa ±63.98) and (5.63 GPa ±0.14), respectively. For EDS analysis, AR and SM groups showed similar elemental composition. In FTIR-ATR analysis, higher peaks referring to the crystalline structure were found for SM group. XRD analysis indicated a decreased formation of Li2O5Si2 from Lithium metasilicate (Li2O-SiO2) in the AM group. SEM micrographs showed a more porous microstructure associated with the 3D printed samples. SIGNIFICANCE: The viability of fabricating Li2O5Si2 ceramic constructs using the Robocasting technique was successful. However, the samples prepared using subtractive manufacturing presented higher mechanical properties compared to the 3D printed constructs. The difference in properties between the manufacturing may be correlated to the decreased formation of Li2O5Si2 crystals and higher degrees of porosity.

Doenças peri-implantares e fatores de risco associados ao paciente, que levam a perda do implante - uma revisão / Peri-implant diseases and risk fatores associated with the patient, leading to loss of the implant - a review

Os tecidos moles periodontais e peri- implantares possuem muitas características em comum, tanto clínicas como histológicas. Para controle e manutenção adequados destes tecidos, é necessário melhor entendimento das diferenças e similaridades que existem entre eles. Os biofilmes se formam em todas as superfícies aderentes em sistemas fluidos, tanto em dentes como em implantes orais. Como um resultado da presença bacteriana, o hospedeiro responde desenvolvendo um mec anismo de defesa que levará à inflamaç ão dos tecidos moles. Na unidade dentogengival, os resultados são as lesões de gengivite. Na unidade implantar, essa inflamaç ão é denominada de muc osite. Se for permitido o acúmulo de placa por períodos prolongados de tempo, pesquisas experimentais demonstraram que a muc osite pode evoluir para peri-implantite, isto na dependência dos fatores e indicadores de risc o, afetando o osso peri- implantar de suporte circunferencialmente. Embora o osso de suporte seja perdido coronalmente, o implante ainda permanec erá ósseo integrado e, portanto, clinicamente estável. Essa é a razão pela qual a mobilidade representa uma característica de diagnóstico de peri-implantite pouco sensível, mas específica. Parâmetros mais sensíveis e confiáveis do desenvolvimento e da presença de infecções peri- implantares são o sangramento a sondagem, profundidade de sondagem e a interpretações radiográficas , visam detectar o mais cedo possível as lesões peri-implantares, possibilitando assim que o tratamento, que nessa revisão é descrito como sendo cumulativo, começ ando por procedimentos mais simples até os mais avançados, tendo em vista, paralisar e evitar a progressão dessas lesões, o que fatalmente resultaria no fracasso do implante.

Implantes imediatos, e seus defeitos peri-implantares (GAP) preenchidos com o uso de biomateriais sintéticos / Implants, and their peri-implant defects (GAP) filled with the use of synthetic biomaterials

A colocação de implantes osseointegráveis requer volume ósseo adequado, porém, a extração de dentes leva a diferentes padrões de remodelaç ão e reabsorção óssea. A reabsorção do rebordo alveolar tem sido considerada uma consequência inevitável da extração dentária e pode ser um problema significativo em Implantodontia. Após a extração dentária, mesmo com a instalação de implantes imediatos, o sítio desdentado do processo alveolar sofre substancial modelagem óssea, com a diminuiç ão das dimensões da crista alveolar. Após a inserção de um implante em um local de extração fresco, um defeito marginal (GAP) ocorre, frequentemente, entre o rebordo e a superfície do implante, A fim de superar esse problema e para facilitar a formaç ão de osso no defeito marginal, vários processos de enxerto têm sido utilizados, associados ou não ao uso de membranas de barreira, bem como diversos tipos de substitutos ósseos que podem ser utilizados para tal procedimento. Esse trabalho tem por objetivo revisar e discutir a literatura relacionada ao uso de biomateriais sintéticos para preenchimento desses defeitos que se formam ao redor de implantes instalados em alvéolos frescos. No entanto, ainda não existe um biomaterial ideal que possua todas as pro- priedades desejáveis. Além disso, o volume de osso residual deve ser avaliado antes da extração de dentes, de modo que os cirurgiões possam utilizar técnicas diferentes para preservar o osso alveolar.

Dietary Intake of Flaxseed Oil since Early Stages of Life Promotes Femur Quality in Male Rats.

BACKGROUND: Flaxseed oil (FO) is an alpha linolenic acid source important for growth and body development. However, there is little literature on the role of FO in critical stages of bone development and formation. OBJECTIVE: This study evaluated the influence of a diet containing FO on rat femurs. METHODS: After birth, mothers and pups were divided into control and flaxseed groups (n = 6 pups each) fed diets containing 7% soybean oil (C) or 7% FO. At 21 days, pups were weaned and separated from the mothers, and control or experimental diets were continued. At 67 days, the following were analyzed: osteocalcin and osteoprotegerin (OPG) levels, bone mineral density (BMD) and content, and bone area; the dimension, BMD, head radiodensity, and biomechanical proprieties of the right femur; and histomorphometric parameters of the left femur. RESULTS: Compared to the C group, the FO group presented (p < 0.05) a lower body mass (-3.7%) and medullary area (-10.1%) and higher osteocalcin (+36.7%), OPG (+52.5%), femur width (+3.8%), absolute mass (+2.3%), femur BMD (+3.6%), head radiodensity (+6.1%), maximum force (+7.4%), breaking strength (+17.3), and cortical thickness (+7.0). CONCLUSION: The FO diet contributed to femur quality in healthy male Wistar rats.

O consumo de farinha de taro (Colocasia esculenta) favorece a integridade óssea em ratos machos / Taro (Colocasia esculenta) flour intake enable bone integrity in male rats

Objetivo: A proposta deste estudo foi investigar a composição óssea em ratos tratados com dieta suplementada com farinha de taro (Colocasia esculenta) até eles completarem 90 dias de idade. Métodos: No momento do desmame, os ratos foram divididos em grupo controle (C, n = 11) e experimental (T, n = 12) ­ composto por animais tratados com farinha de taro até os 90 dias de idade. Ingestão alimentar, massa e comprimento corporal foram avaliados semanalmente ao longo de todo o período experimental. Dimensões ósseas, bem como a densidade mineral óssea (DMO), conteúdo mineral ósseo (CMO), área óssea total e propriedades biomecânicas foram determinadas no final de 90 dias. Resultados: Grupo T apresentou elevados valores (P<0.05) para massa e comprimento corporal; DMO, CMO e área óssea da coluna vertebral; DMO na quarta vértebra lombar; massa femoral, distância entre as epífises, largura do ponto médio da diáfise, DMO, força máxima e concentrações séricas de osteocalcina, quando comparado ao grupo controle. Conclusões: A ingestão da farinha de taro apresentou efeito positivo na saúde óssea. (AU)

Objective: This study aimed to investigate bone composition in male rats treated with diet supplemented with taro (Colocasia esculenta) flour until their 90 days. Methods: Weanling male rats were divided into control (C, n=11) and experimental group (T, n=12); the latter comprised animals treated with taro flour until their 90 days. Food intake, body mass and length were evaluated on a weekly basis throughout the experimental period. Spine bone dimension, as well as bone mineral density (BMD), mineral content (BMC), total area and biomechanical properties were determined after 90 days. Results: T group recorded higher values for (P<0.05) body mass and length; BMD, BMC and total spinal area; BMD of the fourth lumbar vertebra; femoral mass, distance between epiphysis, medial point of diaphysis width, BMD, maximum strength and osteocalcin concentrations than the control. Conclusion: Taro flour intake had positive effect on bone health. (AU)

Resin-dentin bond stability of etch-and-rinse adhesive systems with different concentrations of MMP inhibitor GM1489.

Enzymatic degradation of the hybrid layer can be accelerated by the activation of dentin metalloproteinases (MMP) during the bonding procedure. MMP inhibitors may be used to contain this process. Objective To evaluate the degree of conversion (DC%), dentin bond strength (µTBS) (immediate and after 1 year of storage in water), and nanoleakage of an experimental (EXP) and a commercial (SB) adhesive system, containing different concentrations of the MMP inhibitor GM1489: 0, 1 µM, 5 µM and 10 µM. Methodology DC% was evaluated by FT-IR spectroscopy. Dentin bond strength was evaluated by µTBS test. Half of beams were submitted to the µTBS test after 24 h and the other half, after storage for 1 year. From each tooth and storage time, 2 beams were reserved for nanoleakage testing. Data were analyzed using ANOVA and Tukey's test to compare means (α=0.05). Results All adhesive systems maintained the µTBS after 1 year of storage. Groups with higher concentrations of inhibitor (5 µM and 10 µM) showed higher µTBS values than groups without inhibitor or with 1 µM. The nanoleakage values of all groups showed no increase after 1 year of storage and values were similar for SB and EXP groups, in both storage periods. The inhibitor did not affect the DC% of the EXP groups, but the SB5 and SB10 groups showed higher DC% values than those of SB0 and SB1. Conclusions The incorporation of GM1489 in the adhesive systems had no detrimental effect on DC%. The concentrations of 5 µM GM1489 for SB and 5 µM or 10 µM for EXP provided higher µTBS than groups without GM1489, in the evaluation after 1 year of storage; whereas the concentration of inhibitor did not affect adhesive systems nanoleakage.

Resin-dentin bond stability of etch-and-rinse adhesive systems with different concentrations of MMP inhibitor GM1489

Abstract Enzymatic degradation of the hybrid layer can be accelerated by the activation of dentin metalloproteinases (MMP) during the bonding procedure. MMP inhibitors may be used to contain this process. Objective To evaluate the degree of conversion (DC%), dentin bond strength (µTBS) (immediate and after 1 year of storage in water), and nanoleakage of an experimental (EXP) and a commercial (SB) adhesive system, containing different concentrations of the MMP inhibitor GM1489: 0, 1 µM, 5 µM and 10 µM. Methodology DC% was evaluated by FT-IR spectroscopy. Dentin bond strength was evaluated by µTBS test. Half of beams were submitted to the µTBS test after 24 h and the other half, after storage for 1 year. From each tooth and storage time, 2 beams were reserved for nanoleakage testing. Data were analyzed using ANOVA and Tukey's test to compare means (α=0.05). Results All adhesive systems maintained the µTBS after 1 year of storage. Groups with higher concentrations of inhibitor (5 µM and 10 µM) showed higher µTBS values than groups without inhibitor or with 1 µM. The nanoleakage values of all groups showed no increase after 1 year of storage and values were similar for SB and EXP groups, in both storage periods. The inhibitor did not affect the DC% of the EXP groups, but the SB5 and SB10 groups showed higher DC% values than those of SB0 and SB1. Conclusions The incorporation of GM1489 in the adhesive systems had no detrimental effect on DC%. The concentrations of 5 µM GM1489 for SB and 5 µM or 10 µM for EXP provided higher μTBS than groups without GM1489, in the evaluation after 1 year of storage; whereas the concentration of inhibitor did not affect adhesive systems nanoleakage.

Topography and Microhardness Changes of Nanofilled Resin Composite Restorations Submitted to Different Finishing and Polishing Systems and Erosive Challenge

Abstract Objective: To evaluate the topography and microhardness of composite resin restorations submitted to different finishing and polishing systems before and after erosive challenge. Material and Methods: Thirty standardized cavities prepared in enamel-dentin blocks of bovine incisors were restored with Z350 composite resin, and randomly distributed into three groups (n=10) according to the finishing and polishing systems: G1 = Soflex 4 steps, G2 = Soflex Spiral 2 steps and G3 = PoGo (single step). The specimens were half protected with nail varnish and submitted to five immersions in Pepsi Twist®, for 10 minutes each, five times/day during six consecutive days. The initial and final challenge surface microhardness (SMHinitial and SMHfinal) of the composite resin was evaluated and the percentage of SMH loss (%SMHL) was calculated. After protection removal, the topographic change linear (Ra) and volumetric (Sa) roughness was evaluated in initial and final areas by using 3D non-contact optical profilometry and scanning electron microscopy (SEM). Data were analyzed by paired Student's t-test, Kruskal-Wallis test, and by ANOVA and Tukey's test. Results: There was significant intra-group %SMHL in composite resin (p<0.05). Differences among groups in %SMHL, Ra/Sa in resin composite were not observed (p>0.05). SEM images revealed structural changes between the initial and final surfaces for all groups. Conclusion: The three types of finishing and polishing systems had a similar influence on %SMHL, Ra and Sa in the nanofilled composite resin.

Can the Use of a Warm-Air Stream for Solvent Evaporation Lead to a Dangerous Temperature Increase During Dentin Hybridization?

PURPOSE: To analyze the effect of a warm-air stream for solvent evaporation on the temperature rise in the pulp chamber during dentin hybridization. MATERIALS AND METHODS: Dentin disks with thicknesses of 0.5, 1.0 and 1.5 mm were obtained from extracted human molars. A model tooth was set up with the dentin disks between a molar with an exposed pulp chamber and a crown with an occlusal preparation. A K-type thermocouple connected to a digital thermometer was placed in the molar root until it entered the pulp chamber and made contact with the dentin disks. After 10 s of adhesive application, solvent evaporation was performed for 10, 20, 30, and 40 s and the increase in temperature was monitored for 200 s after the warm-air stream began. RESULTS: The temperature increase was significantly influenced by the thickness of the dentin disks (0.5 mm = 1.0 mm > 1.5 mm). With respect to the duration of the warm-air stream, the temperature increase was as follows: 10 s < 20 s < 30 s < 40 s (p < 0.05). The highest temperature was found after 40 s with dentin disks that were 0.5 mm (16.6°C) and 1.0 mm (15.8°C) thick, whereas the lowest temperature increase occurred after 10 s with a dentin disk that was 1.5 mm thick (4.1°C) (p < 0.05). CONCLUSION: The temperature in the pulp chamber was strongly influenced by the dentin thickness and the duration of the warm-air stream. Thinner dentin and a longer duration of the warm-air stream both lead to a greater temperature increase in the pulp chamber.

Model resin composites incorporating ZnO-NP: activity against S. mutans and physicochemical properties characterization.

Although resin composites are widely used in the clinical practice, the development of recurrent caries at composite-tooth interface still remains as one of the principal shortcomings to be overcome in this field. Objectives To evaluate the activity against S. mutans biofilm of model resin composites incorporating different concentrations of ZnO-nanoparticles (ZnO-NP) and characterize their physicochemical properties. Materials and Methods Different concentrations of ZnO-NP (wt.%): E1=0, E2=0.5, E3=1, E4=2, E5=5 and E6=10 were incorporated into a model resin composite consisting of Bis-GMA-TEGDMA and barium borosilicate particles. The activity against S. mutans biofilm was evaluated by metabolic activity and lactic acid production. The following physicochemical properties were characterized: degree of conversion (DC%), flexural strength (FS), elastic modulus (EM), hardness (KHN), water sorption (Wsp), water solubility (Wsl) and translucency (TP). Results E3, E4, E5 and E6 decreased the biofilm metabolic activity and E5 and E6 decreased the lactic acid production (p<0.05). E6 presented the lowest DC% (p<0.05). No significant difference in FS and EM was found for all resin composites (p>0.05). E5 and E6 presented the lowest values of KHN (p<0.05). E6 presented a higher Wsp than E1 (p<0.05) and the highest Wsl (p<0.05). The translucency significantly decreased as the ZnO- NP concentration increased (p<0.05). Conclusions The incorporation of 2 - 5 wt.% of ZnO-NP could endow antibacterial activity to resin composites, without jeopardizing their physicochemical properties.

Effect of Calcium Hydroxide on Bonding Performance of an Experimental Self-etch Adhesive.

PURPOSE: To investigate the effect of Ca(OH)2 concentration on pH neutralization, degree of conversion (DC%), and bonding performance of experimental self-etch adhesives (SEAs). MATERIALS AND METHODS: Four different concentrations of Ca(OH)2 (0 wt%, 1 wt%, 2 wt%, and 4 wt%) were added to the bond of an experimental two-step SEA consisting of primer (10-MDP [30 wt%], TEG-DMA [30 wt%], ethanol [35 wt%], water [5 wt%], camphorquinone [0.5 wt%], and tertiary amine [0.5 wt%]) and bond (bis-GMA [50 wt%], TEG-DMA [30 wt%], HEMA [20 wt%], camphorquinone [0.5 wt%], and tertiary amine [0.5 wt%]) to form four groups: E0, E1, E2 and E4. pH neutralization was evaluated until it reached equilibrium, and DC% within the hybrid layer was analyzed by micro-Raman spectroscopy. Human molars were wet ground until the occlusal dentin was exposed, SEAs were applied, and composite buildups were constructed. After storage in distilled water at 37°C for 24 h, the teeth were cut into composite-dentin beams. Microtensile bond strength (µTBS) was evaluated after 24 h of water storage at 37°C. Nanoleakage was evaluated by SEM. Data were analyzed using ANOVA and Tukey's HSD test (a = 0.05). RESULTS: All the SEAs reached pH equilibrium after thirteen days, with E1 and E4 presenting the highest pH (p < 0.05). E0 and E1 presented lower DC% than did E2 and E4 (p < 0.05). All the SEAs showed statistically similar mTBS and nanoleakage (p > 0.05). CONCLUSION: The incorporation of Ca(OH)2 endowed the SEAs with pH-neutralization ability and improved their DC%, without interfering with the bond strength to dentin or nanoleakage extent.

Can whitening toothpastes maintain the optical stability of enamel over time?

Besides the effects on the health of individuals, cigarette smoking can also interfere with the appearance of their teeth. To evaluate the effect of cigarette smoking-toothbrushing-cycling (CSTC) with whitening toothpastes on the roughness and optical behavior of bovine enamel for eight weeks. Thirty bovine dentin/enamel discs, 8.0 mm in diameter and 2.0 mm thick, were randomly divided into three groups according to the toothpastes: whitening (Colgate Luminous White - CW and Oral B 3D White - OW), and a non-whitening (Colgate - C). The roughness, color (CIE L*a*b* system), translucency and gloss were measured before and after the specimens were submitted to CSTC. The topography of the specimens was analyzed by scanning electron microscopy. During the first week, the specimens were daily subjected to the consumption of 20 cigarettes and brushed (40 strokes/100 g) with the toothpastes' slurries. Thereafter, the CSTC was weekly applied in an accumulated model (140 cigarettes/280 strokes) for seven weeks. The data were submitted to two-way ANOVA, Tukey's HSD test, and paired-t test (α=0.05). The three toothpastes produced significant changes in roughness, color, translucency and gloss (p<0.05). After eight weeks, the roughness and the gloss produced by the three toothpastes were similar (p>0.05), while OW produced the lowest color change and the translucency of C was lower than that of CW (p<0.05). The three toothpastes produced a significant decrease in L* values and a significant increase in a* values after eight weeks (p<0.05). No significant difference in the b* coordinate was found for OW (p=0.13) There were topographic changes in the enamel surfaces. The whitening toothpastes increased the roughness, changed the topography and were not able to maintain the optical stability of enamel exposed over eight weeks.

Can whitening toothpastes maintain the optical stability of enamel over time?

Abstract Besides the effects on the health of individuals, cigarette smoking can also interfere with the appearance of their teeth. Objective: To evaluate the effect of cigarette smoking-toothbrushing-cycling (CSTC) with whitening toothpastes on the roughness and optical behavior of bovine enamel for eight weeks. Material and Methods: Thirty bovine dentin/enamel discs, 8.0 mm in diameter and 2.0 mm thick, were randomly divided into three groups according to the toothpastes: whitening (Colgate Luminous White - CW and Oral B 3D White - OW), and a non-whitening (Colgate - C). The roughness, color (CIE L*a*b* system), translucency and gloss were measured before and after the specimens were submitted to CSTC. The topography of the specimens was analyzed by scanning electron microscopy. During the first week, the specimens were daily subjected to the consumption of 20 cigarettes and brushed (40 strokes/100 g) with the toothpastes' slurries. Thereafter, the CSTC was weekly applied in an accumulated model (140 cigarettes/280 strokes) for seven weeks. The data were submitted to two-way ANOVA, Tukey's HSD test, and paired-t test (α=0.05). Results: The three toothpastes produced significant changes in roughness, color, translucency and gloss (p<0.05). After eight weeks, the roughness and the gloss produced by the three toothpastes were similar (p>0.05), while OW produced the lowest color change and the translucency of C was lower than that of CW (p<0.05). The three toothpastes produced a significant decrease in L* values and a significant increase in a* values after eight weeks (p<0.05). No significant difference in the b* coordinate was found for OW (p=0.13) There were topographic changes in the enamel surfaces. Conclusions: The whitening toothpastes increased the roughness, changed the topography and were not able to maintain the optical stability of enamel exposed over eight weeks.

Model resin composites incorporating ZnO-NP: activity against S. mutans and physicochemical properties characterization

Abstract Although resin composites are widely used in the clinical practice, the development of recurrent caries at composite-tooth interface still remains as one of the principal shortcomings to be overcome in this field. Objectives To evaluate the activity against S. mutans biofilm of model resin composites incorporating different concentrations of ZnO-nanoparticles (ZnO-NP) and characterize their physicochemical properties. Materials and Methods Different concentrations of ZnO-NP (wt.%): E1=0, E2=0.5, E3=1, E4=2, E5=5 and E6=10 were incorporated into a model resin composite consisting of Bis-GMA-TEGDMA and barium borosilicate particles. The activity against S. mutans biofilm was evaluated by metabolic activity and lactic acid production. The following physicochemical properties were characterized: degree of conversion (DC%), flexural strength (FS), elastic modulus (EM), hardness (KHN), water sorption (Wsp), water solubility (Wsl) and translucency (TP). Results E3, E4, E5 and E6 decreased the biofilm metabolic activity and E5 and E6 decreased the lactic acid production (p<0.05). E6 presented the lowest DC% (p<0.05). No significant difference in FS and EM was found for all resin composites (p>0.05). E5 and E6 presented the lowest values of KHN (p<0.05). E6 presented a higher Wsp than E1 (p<0.05) and the highest Wsl (p<0.05). The translucency significantly decreased as the ZnO- NP concentration increased (p<0.05). Conclusions The incorporation of 2 - 5 wt.% of ZnO-NP could endow antibacterial activity to resin composites, without jeopardizing their physicochemical properties.

Characterization and coating stability evaluation of nickel-titanium orthodontic esthetic wires: an in vivo study.

The objective of this study was to compare coating dimensions and surface characteristics of two different esthetic covered nickel-titanium orthodontic rectangular archwires, as-received from the manufacturer and after oral exposure. The study was designed for comparative purposes. Both archwires, as-received from the manufacturer, were observed using a stereomicroscope to measure coating thickness and inner metallic dimensions. The wires were also exposed to oral environment in 11 orthodontic active patients for 21 days. After removing the samples, stereomicroscopy images were captured, coating loss was measured and its percentage was calculated. Three segments of each wire (one as-received and two after oral exposure) were observed using scanning electron microscopy for a qualitative analysis of the labial surface of the wires. The Lilliefors test and independent t-test were applied to verify normality of data and statistical differences between wires, respectively. The significance level adopted was 0.05. The results showed that the differences between the wires while comparing inner height and thickness were statistically significant (p < 0.0001). In average, the most recently launched wire presented a coating thickness twice that of the control wire, which was also a statistically significant difference. The coating loss percentage was also statistically different (p = 0.0346) when the latest launched wire (13.27%) was compared to the control (29.63%). In conclusion, the coating of the most recent wire was thicker and more uniform, whereas the control had a thinner coating on the edges. After oral exposure, both tested wires presented coating loss, but the most recently launched wire exhibited better results.

Preventive Effect of CPP-ACPF Paste and Fluoride Toothpastes Against Erosion and Erosion Plus Abrasion In Vitro - A 3D Profilometric Analysis.

PURPOSE: To evaluate the effect of CPP-ACPF paste and fluoride toothpastes on enamel subjected to erosion and erosion plus abrasion in vitro. MATERIALS AND METHODS: A total of 220 human enamel blocks were divided into eleven groups (n = 20): CPP-ACPF paste (MPP), potassium nitrate/sodium fluoride toothpaste (PE), sodium fluoride toothpaste (FD), fluoride-free toothpaste (SO) and control (erosion only with no paste or toothpastes; CO) according to the experimental design: erosion or erosion plus abrasion immediately after erosion (ERO+I-ABR) or 30 min after erosion (ERO+30min-ABR). For 5 days, the specimens were subjected to: (1) erosive challenge (EC) (cola drink, 4 x 5 min/day), topical application of the undiluted paste or diluted toothpastes (1:2 w/w) (4 x 1 min/ day) plus 1 h in artificial saliva (AS) between cycles and overnight; or (2) EC plus abrasion (4 x /60 s/day) performed with the diluted toothpastes (no MMP) plus 1 h in AS between cycles and overnight. Erosion depth was quantified through a 3D profilometer. Data were analysed using Kruskal-Wallis, Mann-Whitney and Wilcoxon tests (p = 0.05). RESULTS: CPP-ACPF paste and NaF toothpaste showed lowest enamel wear among groups and reduced tissue loss by 89% in erosion challenge. Abrasion led to higher enamel wear than erosion only (p = 0.030). ERO+30min-ABR had no protective effect when compared to ERO+I-ABR (p > 0.05). CONCLUSION: A high frequency of CPP-ACPF paste application (4x daily) is effective in reducing the effects of erosion. A waiting period before performing toothbrushing does not protect enamel against erosion regardless the composition of the toothpastes.

Characterization of Conventional and High-Translucency Y-TZP Dental Ceramics Submitted to Air Abrasion.

This study evaluated the effect of air-abrasion on t®m phase transformation, roughness, topography and the elemental composition of three Y-TZP (Yttria-stabilized tetragonal zirconia polycrystal) dental ceramics: two conventional (Lava Frame and IPS ZirCad) and one with high-translucency (Lava Plus). Plates obtained from sintered blocks of each ceramic were divided into four groups: AS (as-sintered); 30 (air-abrasion with 30 mm Si-coated Al2O3 particles); 50 (air-abrasion with 50 mm Al2O3 particles) and 150 (air-abrasion with 150 mm Al2O3 particles). After the treatments, the plates were submitted to X-ray diffractometry; 3-D profilometry and SEM/EDS. The AS surfaces were composed of Zr and t phases. All treatments produced t®m phase transformation in the ceramics. The diameter of air-abrasion particles influenced the roughness (150>50>30>AS) and the topography. SEM analysis showed that the three treatments produced groove-shaped microretentions on the ceramic surfaces, which increased with the diameter of air-abrasion particles. EDS showed a decrease in Zr content along with the emergence of O and Al elements after air-abrasion. Presence of Si was also detected on the plates air-abraded with 30 mm Si-coated Al2O3 particles. It was concluded that irrespective of the type and diameter of the particles, air-abrasion produced t®m phase transformation, increased the roughness and changed the elemental composition of the three Y-TZP dental ceramics. Lava Plus also behaved similarly to the conventional Y-TZP ceramics, indicating that this high translucency ceramic could be more suitable to build monolithic ceramic restorations in the aesthetic restorative dentistry field.